Rilsan® BMNO P40 TLD
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VfxB33_Rilsan-BMNO-P40-TLD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® BMNO P40 TLD is a polyamide 11 produced from a renewable source. This natural grade is plasticized and designed for injection molding. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 30°C, 24 hr, 2.00 mm | 1.0 | % | |
| Flow : 30°C, 24 hr, 2.00 mm | 1.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 66 | ||
| Shore D, 15 sec | 58 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 345 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 25.0 | MPa | |
| Break | 55.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 42 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 315 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 181 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA11-P, MHLR, 12-003 | ISO 1874 | |
| Renewable Carbon Conent | > 88 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 210 to 280 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEMICOSIL® 989/1K | Wacker Chemie AG | Silicone | SEMICOSIL® |
| Next Nylon 66 Prime Series PMGHS40-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Electrafil® PC 03906 MB | Techmer Engineered Solutions | PC | Electrafil® |
| ESENTTIA 40H92N | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |
| Plaslube® PA6/6 CF30 TS15 BK | Techmer Engineered Solutions | Nylon 66 | Plaslube® |