Ultramid® SEG7
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vf9Zw4_Ultramid-SEG7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid SEG7 is a 35% glass reinforced, injection molding type 6 nylon requiring high strength, surface aesthetics, and good processability. This product has excellent surface appearance while maintaining a good balance of physical properties, such as high strength, improved toughness, and chemical resistance. It features superior flow properties, and is suited for parts having thinner walls and those requiring long lengths. It shows lower pressure, temperature, and cycle time requirements than conventional grades. Applications Applications include power tool, but can be used wherever strength and appearance are critical requirements, for example, automotive applications (door handles and mirrors). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | |
| Water Absorption | |||
| 24 hr | 1.0 | % | ASTM D570 |
| 23°C, 24 hr | 1.0 | % | ISO 62 |
| Saturation | 6.3 | % | ASTM D570 |
| Saturation, 23°C | 6.3 | % | ISO 62 |
| Equilibrium, 50% RH | 1.7 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.7 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 185 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 3.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (23°C) | 9670 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 290 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Drop Impact Resistance (23°C) | 3.80 | J | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 220 | °C | ASTM D3418, ISO 3146 |
| RTI Elec | UL 746 | ||
| 0.710 mm | 130 | °C | |
| 1.50 mm | 140 | °C | |
| 3.00 mm | 140 | °C | |
| RTI Imp | UL 746 | ||
| 0.710 mm | 115 | °C | |
| 1.50 mm | 115 | °C | |
| 3.00 mm | 120 | °C | |
| RTI Str | UL 746 | ||
| 0.710 mm | 120 | °C | |
| 1.50 mm | 120 | °C | |
| 3.00 mm | 140 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene HDPE HL 535 | TOTAL Refining & Chemicals | HDPE, MMW | TOTAL Polyethylene |
| NEOFLON™ EP-526 | Daikin Fluorochemicals (China) Co., Ltd. | ETFE | NEOFLON™ |
| KumhoSunny PC/ASA HSC7045 | Shanghai KumhoSunny Plastics Co., Ltd. | ASA+PC | KumhoSunny PC/ASA |
| OmniPro™ CPP TF20 | OMNI Plastics, LLC | PP Copolymer | OmniPro™ |
| TECHNYL® C 52G1 V30 GREY 2408CF | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |