Latilub 80-17ST G/30
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilub |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VeTGfR_Latilub-80-17ST-G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Self-lubricating product based on Polyphenylene Sulphide (PPS). Silicone / PTFE. Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.67 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.60 to 0.75 | % | |
| Flow : 2.00 mm | 0.25 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 135 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.7 | % | ISO 527-2/5 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.16 | ||
| vs. Itself - Static | 0.19 | ||
| Wear Factor | 90 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 275 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 265 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 255 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 290 to 310 | °C | |
| Mold Temperature | 130 to 150 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® 3525 VP | Wacker Chemie AG | Silicone | POWERSIL® |
| Ranger PBT PBT-201-G20 272 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Evoprene™ GC 641 | AlphaGary | SEBS | Evoprene™ GC |
| Flontech® FT-905-SH | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| POLYfill PPH K20020 D | Polykemi AB | PP Homopolymer | POLYfill |