TAROLOX 10 Z2
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VePLnQ_TAROLOX-10-Z2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAROLOX 10 Z2 is a Polybutylene Terephthalate (PBT) product. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 to 1.28 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/1.2 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 1.6 to 1.8 | % | |
| Flow | 1.6 to 1.8 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.080 | % | |
| Saturation, 23°C | 0.50 | % | |
| Granule Humidity 1 | < 0.050 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 55.0 | MPa | |
| Break | 45.0 | MPa | |
| Tensile Strain (Break) | > 100 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2100 | MPa | ISO 178 |
| Flexural Stress 3 | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 45 | J/m | |
| 23°C | 85 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed) | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 185 | °C | ISO 306/A50 |
| -- | 165 | °C | ISO 306/B50 |
| Ball Pressure Test (165°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 218 | °C | ISO 11357-3 |
| CLTE - Flow (-30 to 30°C) | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.970 mm | HB | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Oxygen Index | 22 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Pre-heater | 100 to 110 | °C | |
| Drying Time | |||
| -- | 1.0 to 2.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1.0 mm/min |
| 3 . | 1.0 mm/min |
| 4 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Topolymer® 9210-801 | Dongguan Top Polymer Enterprise | TPV | Topolymer® |
| Flexirene® CL 10 U | Versalis S.p.A. | LLDPE | Flexirene® |
| Eltex® MED HD5226EA-M | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® MED |
| ALCOM® PP 620/40 IM UV BL1023-13MCX | ALBIS PLASTIC GmbH | PP, Unspecified | ALCOM® PP |
| Sylvin 6930X06 Brown 7454 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |