XENOY™ 1731 resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ve239y_XENOY-1731-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impact/chemical resistant. UV-Stabilized. Excellent physical property retention in automotive exteriors and OVAD. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Specific Volume | 0.820 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | |||
| 250°C/5.0 kg | 9.6 | g/10 min | ASTM D1238 |
| 250°C/5.0 kg | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Across Flow : 3.20 mm | 0.60 to 0.80 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.28 | % | |
| Equilibrium, 23°C, 50% RH | 0.080 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2370 | MPa | ASTM D638 |
| -- | 2330 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 61.4 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Break 3 | 56.0 | MPa | ASTM D638 |
| Break | 58.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/50 |
| Break 5 | 100 | % | ASTM D638 |
| Break | 90 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2340 | MPa | ASTM D790 |
| -- 7 | 2210 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 93.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 65 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 110 | J/m | ASTM D256 |
| 23°C | 670 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 160 | J/m | ASTM D256 |
| -30°C 10 | 16 | kJ/m² | ISO 180/1A |
| 23°C 11 | 59 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 61.5 | J | |
| 23°C, Total Energy | 61.1 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 116 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 93.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 107 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 99.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 125 | °C | ASTM D1525 13 |
| -- | 127 | °C | ISO 306/B50 |
| -- | 130 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 7.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flow : -40 to 95°C | 8.3E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI Str | 75.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 14 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 to 80 | % | |
| Rear Temperature | 243 to 266 | °C | |
| Middle Temperature | 249 to 271 | °C | |
| Front Temperature | 254 to 277 | °C | |
| Nozzle Temperature | 254 to 271 | °C | |
| Processing (Melt) Temp | 260 to 277 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.013 to 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| 14 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® COC PG13PG BT | Tekni-Films, a div of Tekni-Plex | Film, PETG/COC/PETG | TEKNIFLEX® |
| VERSIFY™ 3200 | The Dow Chemical Company | POP | VERSIFY™ |
| Greenflex® ML 20 | Versalis S.p.A. | EVA | Greenflex® |
| Kepital® F20-52 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Plaskon SMT-B-1 | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |