EcoPaXX® Q-PG6
| Category: | Nylon 410 , Polyamide 410 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | EcoPaXX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VdgX5f_EcoPaXX-Q-PG6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EcoPaXX® Q-PG6 is a Polyamide 410 (Nylon 410) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Important attributes of EcoPaXX® Q-PG6 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.30 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.3 | -- | % | |
| Flow | 0.67 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.4 | -- | % | ISO 62 |
| Calculated Bio-based Carbon Content | 66 | -- | % | ASTM D6866 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8000 | 6000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 150 | 110 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 4.5 | 5.8 | % | ISO 527-2 |
| Flexural Modulus | 7500 | 5800 | MPa | ISO 178 |
| Flexural Stress | 220 | 160 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 14 | -- | kJ/m² | |
| 23°C | 20 | 25 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 85 | 90 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 240 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 250 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 5.5E-5 | -- | cm/cm/°C | |
| Transverse | 6.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | > 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 40 | 38 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 300 | °C | |
| Processing (Melt) Temp | 275 to 310 | °C | |
| Mold Temperature | 80.0 to 140 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC NFC87-80E | Vi-Chem Corporation | PVC, Rigid | Vi-Chem PVC |
| Triapol® Blends C3 K55 CNZ0062 BS301 | Petropol Industry and Trade of Polymers LTDA | PC+ABS | Triapol® Blends |
| Colorite Rigid PVC 1124-03 | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| Indothene HD HD55EF010 | Reliance Industries Limited | HDPE | Indothene HD |
| LNP™ LUBRICOMP™ RAL22 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |