| Polyacetal copolymer, lubricated with molybdenum disulfide, recommended in cases where it is desired characteristics of sliding. Suitable for injection |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 to 1.44 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 25 to 28 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.8 to 2.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 61.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 2600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 160 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 100 | °C | |
| Peak Melting Temperature | 170 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dissipation Factor (1 MHz) | 6.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4602 TFE 15 SI 2 | RTP Company | SPS | RTP |
| Multilon® T-2754 | TEIJIN LIMITED | PC+ABS | Multilon® |
| Network Polymers PP PPB 25 1010 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| Clariant Nylon 6/6 PA-123G33 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| POCAN® KU 1-7635 POS 151 000000 | LANXESS GmbH | PC+PBT | POCAN® |