Hybrid S555
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Ravago Manufacturing Americas, LLC |
| Trademark: | Hybrid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VbwhqP_Hybrid-S555.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS, High Flow, Non-Halogenated Flame Retardant |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 63.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 45 | % | ISO 527-2 |
| Flexural Modulus | 2550 | MPa | ISO 178 |
| Flexural Stress | 84.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 46 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 107 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 94.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 110 | °C | ISO 306 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.50 mm | V-0 5VB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC GPT 45 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| WanBlend® WHT-HF9485K2 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | WanBlend® |
| Etinox® ER-B121 | Ercros, S.A. | PVC, Rigid | Etinox® |
| GLAMIDE® T-402 | TOYOBO America, Inc. | Nylon 6 | GLAMIDE® |
| Hanwha Total PP LH72S | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Homopolymer | Hanwha Total PP |