RTP 200 D FR
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VbqzuK_RTP-200-D-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced - Flame Retardant |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.5 - 2.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.35 | % | ASTM D570 |
| Moisture Content | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength | 44.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.0 - 4.0 | % | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 210 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 179 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 87.8 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(in Oil) | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.50 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.020 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 249 - 285 | °C | |
| Mold Temperature | 60.0 - 93.3 | °C | |
| Injection Pressure | 68.9 - 124 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPC101 | Polyram Ram-On Industries | PP Copolymer | RAMOFIN |
| Sumitomo PP AR564 | Sumitomo Chemical Asia | PP Copolymer | Sumitomo PP |
| Aplax P0213GN | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| Hanwha Total PE R906U | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |
| POLYFORT® FIPP 20 T LE K1832 | A. Schulman Europe | PP Copolymer | POLYFORT® |