Order Products : sales@su-jiao.com
DENISAB 1710
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Vamp Tech |
| Trademark: | DENISAB |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VbKkyE_DENISAB-1710.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS, 17% glass fiber reinforced, not Flame Retardant compound, good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | |
| Across Flow | 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 8.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 15 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 93.0 | °C | ASTM D648A |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 1 |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI Str | 75.0 | °C | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 | °C | |
| Mold Temperature | 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riteflex® 655HS | Celanese Corporation | TPC-ET | Riteflex® |
| Nylfor® B2 FR2/3A NERO | SO.F.TER. SPA | Nylon 6 | Nylfor® |
| APEX® 3200-50NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Forprene® 6NE001D50 | SO.F.TER. SPA | TPV | Forprene® |
| LNP™ LUBRICOMP™ RL003 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |