Later 4 G/30
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Later |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VahTmW_Later-4-G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polybutylene Terephtalate (PBT). Glass fibres. Product UL certified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.0 to 1.3 | % | |
| Flow : 2.00 mm | 0.30 to 0.55 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 10500 | MPa | |
| 60°C | 6900 | MPa | |
| 90°C | 5100 | MPa | |
| 120°C | 4100 | MPa | |
| 150°C | 3200 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 125 | MPa | |
| Break, 60°C | 85.0 | MPa | |
| Break, 90°C | 70.0 | MPa | |
| Break, 120°C | 50.0 | MPa | |
| Break, 150°C | 45.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.0 | % | |
| Break, 60°C | 2.8 | % | |
| Break, 90°C | 3.0 | % | |
| Break, 120°C | 3.1 | % | |
| Break, 150°C | 3.1 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 4.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 35 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 45 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 140 | °C | |
| Vicat Softening Temperature | 210 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Oxygen Index | 23 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 250 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QR Resin QR-4165 | QTR, Inc. | PPE+PS | QR Resin |
| COPYLENE® CH085 | Phillips 66 | PP Homopolymer | COPYLENE® |
| Flontech® FT-1-FM-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| FORMULA P COMP 3220 | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| OTECH PVC OC5817-Sandal | OTECH Corporation | PVC, Unspecified | OTECH PVC |