DINALEN® 65
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | DIOKI d.d. |
| Trademark: | DINALEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VZiyhB_DINALEN-65.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DINALEN® 65 is low density polyethylene containing slip and anti-blocking additives. It is intended for thin blow film extrusion. Other processing techniques can be used in less extent. DINALEN® 65 exhibits excellent processability, uniform optical and other properties, depending on its application. It is extruded at temperatures ranging from 140°C to 165°C. DINALEN® 65 gives films of desired properties depending on selected processing parameters such as processing temperature and capacity; blowing ratio, and the height of the frost line. Recommended film thickness : 0.020 mm to 0.040 mm. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 43 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 10.0 | MPa | |
| Break | 12.0 | MPa | |
| Tensile Strain (Break) | 600 | % | ISO 527-2 |
| Coefficient of Friction | ISO 8295 | ||
| vs. Itself - Dynamic | < 0.11 | ||
| vs. Itself - Static | < 0.11 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Film Thickness - Recommended / Available | 0.020mm to 0.040 mm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 90.0 | °C | ISO 306/A |
| Melting Temperature | 110 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm) | 65 | ASTM D2457 | |
| Haze (38.0 µm) | 2.5 | % | ASTM D2457 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 145 to 165 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-2095-60A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| MTA® 240 | Cytec Industries Inc. | Epoxy | MTA® |
| Vyncolit® E 8705 | Vyncolit N.V. | Epoxy | Vyncolit® |
| Petlon R-Prime B2-G30-00-BK | Petlon Polymers Ltd | Nylon 6 | Petlon R-Prime |
| ESTOPLAST XU 400GY32 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |