| Category: | ETFE , Ethylene Tetrafluoroethylene Copolymer |
| Manufacturer: | DuPont Fluoropolymers |
| Trademark: | Tefzel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VZKRVG_Tefzel-750.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DuPont™ Tefzel ® fluoropolymer resins offer mechanical strength and toughness along with resistance to heat and chemicals. In addition, they provide easy processing, high specific dielectric strength, and a low coefficient of friction. For these reasons, Tefzel ® resins are widely used to make compact wire and cable constructions that provide long, reliable service in demanding environments. Tefzel ® 750 retains the traditional characteristics of Tefzel ® resins while providing some new property advantages, including increased flexibility and improved retention of properties after aging at elevated temperatures, higher limiting oxygen index, and long-term service life at higher temperatures than other Tefzel ® resins. Underwriters Laboratories, Inc. (UL) has rated wire insulated with Tefzel ® 750 (10 mil for 600V, 6 mil for 300V) for service in appliances at a maximum continuous operating temperature of 200°C (392°F). This rating was determined under the guidelines of UL Subject 758 for appliance wiring material. Upper service temperatures for other applications should be determined under the guidelines for those applications. Temperature ratings may not be the same as the rating for appliance wire because the test procedures are different. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 to 1.79 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (297°C/5.0 kg) | 7.0 | g/10 min | ASTM D3159 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D1708 | ||
| 23°C | 37.9 | MPa | |
| 140°C | 11.4 | MPa | |
| 160°C | 8.62 | MPa | |
| 180°C | 6.21 | MPa | |
| 200°C | 3.45 | MPa | |
| Tensile Elongation | ASTM D1708 | ||
| Break, 23°C | 300 | % | |
| Break, 140°C | 600 | % | |
| Break, 160°C | 650 | % | |
| Break, 180°C | 600 | % | |
| Break, 200°C | 600 | % | |
| Flexural Modulus | 645 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 219 to 254 | °C | ASTM D3159 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 34 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 288 | °C | |
| Cylinder Zone 2 Temp. | 316 | °C | |
| Cylinder Zone 3 Temp. | 321 | °C | |
| Adapter Temperature | 321 | °C | |
| Melt Temperature | 332 to 335 | °C | |
| Die Temperature | 332 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex WR-9100SG | SAMSUNG SDI CO., LTD. | ASA | Starex |
| VICTREX® PEEK 90HMF40 | Victrex plc | PEEK | VICTREX® PEEK |
| LNP™ LUBRICOMP™ OL004 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ LUBRICOMP™ |
| Plaskon 7060 | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |
| Sylvin 5153-89 Grey 9452 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |