POCAN® S 1506 901510
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS Corporation |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VZH2hW_POCAN-S-1506-901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, injection molding grade, non-reinforced,Elastomer-modified, high impact strength,Even at low temperatures |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.22 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 23°C, 3.00 mm 1 | 0.50 | % | ISO 294-4 |
| Across Flow : 23°C, 3.00 mm 2 | 1.8 | % | ISO 2577 |
| Flow : 260°C, 3.00 mm 3 | 1.8 | % | ISO 2577 |
| Flow : 150°C, 48 hr, 3.00 mm 4 | 0.50 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 70.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 4.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 1600 | MPa | ISO 178/A |
| Flexural Stress 6 | |||
| 3.5% Strain | 45.0 | MPa | ISO 178/A |
| 23°C | 55.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 5.5 | % |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Electrolytical Corrosion | A 1 | IEC 60426 | |
| ISO Shortname | PBT-I,MHR,11-020 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 to 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 25 | kJ/m² | |
| 23°C | 75 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | |||
| -30°C | 20 | kJ/m² | ISO 180/1A |
| -30°C | No Break | ISO 180/1C | |
| 23°C | 75 | kJ/m² | ISO 180/1A |
| 23°C | No Break | ISO 180/1C |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| Ball Pressure Test (180°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 8 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 1.3E-4 | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.3E-4 | cm/cm/°C | |
| Thermal Conductivity (23°C) | 0.22 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.20 | ||
| 23°C, 1 MHz | 3.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 2.0E-3 | ||
| 23°C, 1 MHz | 0.017 | ||
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 600 | V | |
| Solution B | 600 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Oxygen Index 9 | 22 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 150x105x3 |
| 2 . | 150x150x3 |
| 3 . | 150x150x3; MT 80°C; 600 Bar |
| 4 . | 150x150x3 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOND 5010 | SILON s.ro | PP, Unspecified | TABOND |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 4216 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Complet® LGF40-PP | PlastiComp, Inc. | PP Homopolymer | Complet® |
| RTP 199 X 141363 A | RTP Company | TPO (POE) | RTP |
| VALOX™ 310SE0 resin | SABIC Innovative Plastics | PBT | VALOX™ |