HI-ZEX™ 5000H
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Prime Polymer Co., Ltd. |
| Trademark: | HI-ZEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VYvmdv_HI-ZEX-5000H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HI-ZEX™ 5000H is a High Density Polyethylene product. It can be processed by extrusion and is available in Asia Pacific, Europe, or North America. Applications of HI-ZEX™ 5000H include industrial applications and sheet. Primary characteristic: good stiffness. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.10 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance | > 600 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 1400 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 29.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Compression Molded) | > 500 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 9.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 125 | °C | ISO 306 |
| Melting Temperature | 132 | °C | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Valtra® EA3300 | Saudi Polymers Company | PS (GPPS) | Valtra® |
| Nirion 3550/M | Soredi S.p.a. | PC | Nirion |
| Hanwha Total PP TB32R | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Osterlene® PPH-35-.4 | Osterman & Company | PP Homopolymer | Osterlene® |
| LG ABS AF366 | LG Chem Ltd. | ABS | LG ABS |