Escorene™ Ultra FL 00209
| Category: | EVA , Ethylene Vinyl Acetate Copolymer Resin |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | Escorene™ Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VYsB6m_Escorene-Ultra-FL-00209.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FL 00209 is a copolymer of ethylene and vinyl acetate. When the processing temperature is higher than 270 C (518 °F) in processing conditions, resin degradation may be caused. The machine should be thoroughly cleaned with low density polyethylene or suitable detergent before stopping. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.1 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 9.4 | wt% | ExxonMobil Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 94 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 110 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 100 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 100 | MPa | ASTM D882 |
| 1% secant, TD | 100 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 30.0 | MPa | ASTM D882 |
| TD : Fracture | 26.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 510 | % | ASTM D882 |
| TD : Fracture | 650 | % | ASTM D882 |
| Dart Drop Impact | 370 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 110 | g | ASTM D1922 |
| TD | 170 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 78.0 | °C | ASTM D1525 |
| Legal statement |
|---|
| 有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil G-9340 | NuSil Technology | Silicone | NuSil |
| Clariant Nylon 6/6 6618G15-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| ICORENE® 5704 | ICO Polymers EMEA, A Division of A. Schulman | HDPE | ICORENE® |
| Sylvin 2997-90 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ DF006 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |