TECACOMP® PA66 TRM XS black 4074
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VYcG3z_TECACOMPPA66TRMXSblack4074.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | |
| Apparent Density | 0.64 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 75 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 65.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.0 | % | ISO 294-4 |
| Flow | 0.36 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.8 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18500 | MPa | ISO 527-2/50 |
| Tensile Stress | 200 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 263 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 255 | °C | ISO 75-2/A |
| Glass Transition Temperature | DIN 53765 | ||
| -- 1 | 5.00 | °C | DIN 53765 |
| -- 2 | 72.0 | °C | DIN 53765 |
| Melting Temperature | 260 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 45°C | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 70 to 120°C | 9.0E-6 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 45°C | 7.8E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 70 to 120°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 3 | 0.70 | W/m/K | DIN EN 821 |
| -- 4 | 1.1 | W/m/K | DIN EN 821 |
| Service Temperature | |||
| long term | 110 | °C | |
| short term | 170 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.2E+4 | ohms·cm | ISO 3915 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | Moist |
| 2 . | Dry |
| 3 . | Through-plane |
| 4 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stirolan DF AE V0 1.6 | Soredi S.p.a. | PS (HIPS) | Stirolan |
| Topolymer® 5711-901M | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| TOTAL Polypropylene PPC 3666 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Geon™ Vinyl Flexible P502 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| elitel UE-3700 | UNITIKA Plastics Division | TPC-ET | elitel |