Order Products : sales@su-jiao.com
ACRYPET® IR K304
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Mitsubishi Rayon Co., Ltd. |
| Trademark: | ACRYPET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VXwu6W_ACRYPETIRK304.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ACRYPET®IR K304 is a polymethyl methacrylate-acrylic material,. This product is available in North America or Asia Pacific,. ACRYPET®The main characteristics of IR K304 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.0 | g/10 min | ISO 1133 |
| Spiral Flow | Internal method | ||
| -- 1 | 15.0 | cm | Internal method |
| -- 2 | 27.0 | cm | Internal method |
| Molding Shrinkage | 0.30 - 0.70 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | 65.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 19 | % | ISO 527-2/1A/5 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress | 98.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.6 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 43 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 2.9 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 93.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 98.0 | °C | ISO 306/B |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1500 | J/kg/°C | JIS K7123 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+16 | ohms | JIS K6911 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | JIS K6911 |
| Dielectric Strength 3 | 20 | kV/mm | JIS K6911 |
| Dielectric Constant (60 Hz) | 3.70 | JIS K6911 | |
| Dissipation Factor (60 Hz) | 0.050 | JIS K6911 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance (Total, 3000 µm) | 92.0 | % | ISO 13468 |
| Haze (3000 µm) | 0.50 | % | ISO 14782 |
| Note Message | |
|---|---|
| 1 . | Melt temperature: 230°C |
| 2 . | Melt temperature: 250°C |
| 3 . | 4000 V/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V77W | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| RheTech Thermoplastic Polyolefin FT3080-640UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Vatpol 212 | Vatan Plastik San. Tic. AS | PE, Unspecified | Vatpol |
| ENVIROSUN® ENV31-NC080 | ENVIROPLAS®, Inc. | ASA | ENVIROSUN® |
| Sylvin 2973-80 White 1560 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |