RTP 100 FR HI
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VW4wdE_RTP-100-FR-HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. RTP 100 FR HI is a flame retardant co-polymer polypropylene. Characteristics include excellent impact resistance and low specific gravity. |
| General Information | |
|---|---|
| Additive |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.998 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 2.3 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 17.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 1030 | MPa | ASTM D790 |
| Flexural Strength | 20.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 160 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 93.3 | °C | |
| 1.8 MPa, Unannealed | 54.4 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm, NC, BK, Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 204 to 232 | °C | |
| Middle Temperature | 204 to 232 | °C | |
| Front Temperature | 204 to 232 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PEI-G20 | Polymer Resources Ltd. | PEI | PRL |
| SABIC® PP 412MN40 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| Spartech Polycom SPF7015 | Spartech Polycom | PC | Spartech |
| Nycal™ 2050L | Technical Polymers, LLC | Nylon 612 | Nycal™ |
| Clariant Nylon 6/6 PA-113M40 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |