TECHNYL® B 218 MX30 NATURAL
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VVwEWD_TECHNYLB218MX30NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® B 218 MX30 Natural is a polyamide 66/6, reinforced with 30% of mineral filler, heat stabilized, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.38 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 1.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 7400 | 4000 | MPa | ISO 527-2/1A |
| Tensile Stress (Break, 23°C) | 80.0 | 50.0 | MPa | ISO 527-2/1A |
| Tensile Strain | ISO 527-2 | |||
| Yield, 23°C | 4.0 | 12 | % | ISO 527-2 |
| Fracture, 23°C | 4.0 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 6000 | 2600 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | 110 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 3.0 | 5.0 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 180 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 242 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 6.0E+14 | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 35 | 30 | kV/mm | IEC 60243-1 |
| Dissipation Factor | 0.020 | 0.080 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution a | 550 | 550 | V | IEC 60112 |
| Solution B | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Glow Wire Flammability Index (1.6 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 26 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 255 - 265 | °C | |
| Middle Temperature | 260 - 270 | °C | |
| Front Temperature | 270 - 280 | °C | |
| Mold Temperature | 70 - 100 | °C |
| Injection instructions |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michithene R6100 | API Polymers, Inc. | LDPE | Michithene |
| Moplen HP422H | LyondellBasell Industries | PP Homopolymer | Moplen |
| Chiao Fu PP PP212GB40 NAT | Chiao Fu Enterprises Co., Ltd. | PP, Unspecified | Chiao Fu PP |
| Complet® LGF40-PPA | PlastiComp, Inc. | PPA | Complet® |
| LTP PA6150 | Chengdu Letian Plastics Co., Ltd | TP, Unspecified | LTP |