Pearlbond™ 522
| Category: | TPU-Capro , Thermoplastic Polyurethane Elastomer (Polycaprolactone) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlbond™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VVqu9Q_Pearlbond-522.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pearlbond® 522 is a linear, polycaprolactone-copolyester polyurethane, supplied in form of white spherical granules with a very high crystallization rate and a very high thermoplasticity level. Pearlbond® 522 can be added to formulations of REACTIVE POLYURETHANE HOT-MELTS (HMPUR), in order to improve the crystallisation speed. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (20°C) | 1.19 | g/cm³ | ISO 2781 |
| Melt Mass-Flow Rate (MFR) (170°C/21.6 kg) | 110 to 160 | g/10 min | ISO 1133 |
| Moisture Content | < 1500 | ppm | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Crystallization Rate | 9.0 to 11.0 | min | Internal Method |
| OH Value | < 3.00 | mg KOH/g | Internal Method |
| Thermoplasticity | Very High | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 65.0 to 69.0 | °C | Internal Method |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (130°C) | 4900 | Pa·s | ISO 1133 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2099 X 134503 A | RTP Company | PLA | RTP |
| PRL NY66-GP2-(color)H | Polymer Resources Ltd. | Nylon 66 | PRL |
| RTV-2 P-90 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| TRIBOCOMP® POM TS0 | EPIC Polymers | Acetal (POM) Copolymer | TRIBOCOMP® |
| Beetle® PPC130M 9249 | Teknor Apex Company (Chem Polymer) | PP Copolymer | Beetle® |