20-1634 is a low density, two component silicone elastomer. The 20-1634 is less than half the weight of most commercially available potting and encapsulating compounds. 20-1634 utilizes an advanced micro balloon technology filler. This system is ideal for applications that require low weight, flexibility, high heat resistance, and excellent electrical insulation properties. 20-1634 is formulated without solvents or other toxic materials. It is therefore not regulated or considered hazardous for transportation. Features:
Benefits:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 2.0E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.16 | W/m/K |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Mix Viscosity (25°C) | 30000 | cP |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Operating Temperature | -65.0 to 235 | °C |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 1 | Clear/Transparent | ||
| -- 2 | White | ||
| Mix Ratio by Weight (PBW) | |||
| Part A | 100 | ||
| Part B | 10 | ||
| Density | |||
| 25°C 3 | 0.798 | g/cm³ | |
| 25°C 4 | 0.818 | g/cm³ | |
| 25°C 5 | 0.968 | g/cm³ | |
| Viscosity | |||
| 25°C 6 | 0.10 | Pa·s | |
| 25°C 7 | 45 | Pa·s | |
| Curing Time | |||
| 150°C | 0.33 | hr | |
| 100°C | 1.0 | hr | |
| 65°C | 2.0 to 4.0 | hr | |
| 25°C | 24 to 48 | hr | |
| Pot Life 8(25°C) | 60 | min | |
| Shelf Life | 6 | month |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore A) | 34 | ||
| Tensile Strength | 0.862 | MPa | |
| Tensile Elongation at Break | 230 | % | |
| Tear Strength | 2.89 | kN/m | |
| Electric Strength | 18 | kV/mm | |
| Relative Permittivity (100 Hz) | 3.10 | ||
| Volume Resistivity (25°C) | 1.0E+14 | ohms·cm |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | Part A |
| 4 . | Mixed |
| 5 . | Part B |
| 6 . | Part B |
| 7 . | Part A |
| 8 . | 100 grams |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® HD 5306 | Plastic Solutions, Inc. | HDPE | PrimaFlex® |
| Shandong PA1212 GYBLVN | Shandong Guangyin New Materials Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| Softell CA 02 A | LyondellBasell Industries | Polyolefin, Unspecified | Softell |
| ASTALON™ S3600UR | Marplex Australia Pty. Ltd. | PC | ASTALON™ |
| Plasmer 1380B/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |