Order Products : sales@su-jiao.com
FRAGOM PR/720
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | FRAGOM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VVObkR_FRAGOM-PR-720.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FRAGOM PR PR/720 is a flame retardant polyolefinic compound. FRAGOM PR PR/720 is a halogen-free flame-retardant polyolefinic thermoplastic compound with high values of temperature index and oxygen index, very easy to process and suitable for cable sheathing. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/21.6 kg | 30 | g/10 min | ASTM D1238 |
| 280°C/0.325 kg | 2.0 | g/10 min | IEC 60811 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 52 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 13.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | 150 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (110°C, 168 hr) | 10 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air (110°C, 168 hr) | -15 | % | IEC 60811 |
| Change in Tensile Stress | |||
| in Hydrocarbons | < 10 | % | ENI 018 100 |
| 70°C, 4 hr, in ASTM #2 Oil | < 20 | % | IEC 60811 |
| 70°C, 4 hr, in SAE 20 Oil | < 20 | % | IEC 60811 |
| Change in Tensile Strain at Break | |||
| in Hydrocarbons | < 10 | % | ENI 018 100 |
| 70°C, 4 hr, in ASTM #2 Oil | < 20 | % | IEC 60811 |
| 70°C, 4 hr, in SAE 20 Oil | < 20 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Pressure Test - Penetration 1(90°C) | 35 | % | IEC 60811 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Content | < 0.300 | % | IEC 60754-1 |
| Temperature Index (Burning) 2 | 300 | °C | NES 715 |
| Oxygen Index | 40 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Cylinder Zone 1 Temp. | 110 | °C | |
| Cylinder Zone 2 Temp. | 135 | °C | |
| Cylinder Zone 3 Temp. | 1580 | °C | |
| Cylinder Zone 4 Temp. | 160 | °C | |
| Cylinder Zone 5 Temp. | 165 | °C | |
| Die Temperature | 175 | °C |
| Note Message | |
|---|---|
| 1 . | K=0.6, 4 hr |
| 2 . | 21% O2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 6302 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Chemical Resources HD07960 | Chemical Resources, Inc. | HDPE | Chemical Resources |
| KOPA® KN333HS | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| LNP™ STAT-KON™ DEL13PXC compound | SABIC Innovative Plastics Europe | PC | LNP™ STAT-KON™ |
| XENOY™ X4850 resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |