ZEONEX® RS420
| Category: | COC , Cyclic Olefin Copolymer |
| Manufacturer: | Zeon Corporation |
| Trademark: | ZEONEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VUVpka_ZEONEX-RS420.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ZEONEX® - Cyclo Olefin Polymer (COP) offers excellent optical properties for creating optical parts for cameras and laser beam printers. ZEONEX's high purity is suitable for a wide range of medical packaging products, while its low dielectric constant and loss tangents are appropriate for electrical insulation applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/2.16 kg) | 8.0 | g/10 min | JIS K6719 |
| Water Absorption (Equilibrium) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pencil Hardness | B | JIS K5401 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Injection Velocity | 30.0 to 80.0 | cm³/s | |
| Screw Speed | 20 to 60 | rpm |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2 |
| Tensile Stress | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 140 | % | ISO 527-2 |
| Flexural Modulus | 1600 | MPa | ISO 178 |
| Flexural Stress | 64.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 510 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 110 | °C | ISO 75-2/A |
| Glass Transition Temperature | 136 | °C | JIS K7121 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(1.00 mm) | 40 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 2.0E-4 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 4.0 to 10 | hr | |
| Rear Temperature | 250 to 300 | °C | |
| Middle Temperature | 250 to 300 | °C | |
| Front Temperature | 250 to 300 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Injection Pressure | 50.0 to 180 | MPa | |
| Holding Pressure | 50.0 to 180 | MPa | |
| Back Pressure | 5.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stanyl® TS250F4D | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Mylar® WC (142 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Amodel® AT-1002 HS | Solvay Specialty Polymers | PPA | Amodel® |
| LNP™ LUBRICOMP™ PFL36 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |
| Sylvin 802-85 CLEAR BLUE 841 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |