Clearflex® FG 306
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VUFD0K_Clearflex-FG-306.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex FG 306 is a hexene copolymer linear low density polyethylene (C6-LLDPE), additivated with antioxidant, antiblocking and processing aid, suitable for blown film extrusion. Film manufactured with Clearflex FG 306 are characterised by good balance between rigidity, impact resistance and tear resistance (Elmendorf). Main Application Clearflex FG 306 is recommended for the production of heavy duty bags, both in coextrusion and in blend with LDPE. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.926 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 10 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm, Blown Film | 190 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 225 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, Blown Film | 12.0 | MPa | |
| TD : Yield, 25 µm, Blown Film | 13.0 | MPa | |
| MD : Break, 25 µm, Blown Film | 45.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 36.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 550 | % | |
| TD : Break, 25 µm, Blown Film | 740 | % | |
| Dart Drop Impact 1(25 µm, Blown Film) | 120 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 25.0 µm | 82.0 | kN/m | |
| TD : 25.0 µm | 250.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 110 | °C | ISO 306/A |
| Melting Temperature | 127 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 52 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 13 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 24949 | Teknor Apex Company | TPV | Sarlink® TPV |
| Delrin® PC691 NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| EPO-TEK® E4110-PFC | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| LONGLITE® PBT 3030-104EX | CCP Group | PBT+PET | LONGLITE® PBT |
| PETILEN YY S 00356 | PETKIM Petrokimya Holding A.S. | HDPE | PETILEN |