Braskem PE IA 59
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VTdTE6_Braskem-PE-IA-59.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: IA59 is a High Density Polyethylene, narrow molecular weight homopolymer, produced by solution process for injection molding applications. It offers high processability and low warpage. It contains antioxidant additive. Application: Cases, pails, food and general purpose containers for indoor applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.3 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 2.00 mm, 10% Igepal, Compression Molded, F50) | < 3.00 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 58 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 28.0 | MPa | ASTM D638 |
| Fracture, molding | 25.0 | MPa | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 1300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 75 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 81.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 129 | °C | ASTM D1525 1 |
| Additional Information |
|---|
| Recommended Processing Conditions:IA 59 has been developed for injection molding under conditions comparable to High Density Polyethylene of similar Melt Flow Index. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 160 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PVC BOTTLE GRADE K57 | Marco Polo International, Inc. | PVC, Rigid | MARPOL® PVC |
| TAROLOX 10 G5 | Taro Plast S.p.A. | PBT | TAROLOX |
| Next Nylon 66 Prime Series PG25-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Fainplast PVC CKL 0221/T | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| PEARLCOAT® 163K | Lubrizol Advanced Materials, Inc. | TPU-Polyether | PEARLCOAT® |