Aegis® H35ZI
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Honeywell |
| Trademark: | Aegis® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VT6dog_Aegis-H35ZI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aegis® H35ZI is an unfilled, low viscosity, non-lubricated nylon 6 injection molding homopolymer exhibiting excellent melt flow properties for filling thin sections and reduced cycle times. It exhibits good strength, stiffness, and toughness as well as excellent heat, chemical and abrasion resistance. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (235°C/1.0 kg) | 23 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.3 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 1.6 | % | ASTM D570 |
| Saturation | 9.5 | % | ASTM D570 |
| Balance, 50% RH | 2.7 | % | ASTM D570 |
| Moisture Content | % | ASTM D6869 | |
| Relative viscosity- @ 96% SAV | 2.34 | ||
| Viscosity- FAV | 33.0 - 39.0 | ASTM D789 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2750 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 79.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 4.1 | % | ASTM D638 |
| Fracture, 23°C | 75 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2470 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 96.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 45 | J/m | ASTM D256 |
| 23°C | 46 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 152 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 47.0 | °C | ASTM D648 |
| Melting Temperature | 222 | °C | |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM E831 |
| Additional Information |
|---|
| Extractible Content: < 0.8 % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7450 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| SLOVAMID® 6 GF 25 FRC 3 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Dryflex® WS 40E850 | ELASTO | TPE | Dryflex® |
| Hostacom EYC 186N Black | LyondellBasell Industries | PP Copolymer | Hostacom |
| Durethan® B 38 FKA 000000 | LANXESS GmbH | Nylon 6 | Durethan® |