STERLENE™ BMU130D
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | R&P (Pte.) Ltd. |
| Trademark: | STERLENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VSAXrT_STERLENE-BMU130D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| STERLENE™ BMU130D is a compound designed for automotive exterior applications requiring very high impact resistance with high UV resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1280 | MPa | ISO 527-2/50 |
| Tensile Stress (Yield, 23°C) | 15.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 6.4 | % | |
| Break, 23°C | 55 | % | |
| Flexural Modulus 2(23°C) | 1070 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 20.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Partial Break) | 55 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C, Partial Break) | 49 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 49.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 240 | °C | |
| Mold Temperature | 25.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure B |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYsan FL100 F35 | Polykemi AB | SAN | POLYsan |
| RTP 4099 X 113516 A | RTP Company | PPA | RTP |
| Evoprene™ 076 | AlphaGary | SBS | Evoprene™ |
| DIALAC® KD100W | UMG ABS, Ltd. | AES | DIALAC® |
| Fainplast PVC PM 8030 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |