GLS PP YT06 (PP30 Talc)
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VRWy0T_GLS-PP-YT06-PP30-Talc-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP30 Talc Precolor |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 to 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | > 4.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 28.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 5.0 | % | ASTM D638 |
| Flexural Modulus | > 2800 | MPa | ASTM D790 |
| Flexural Strength | > 46.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | > 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | > 55.0 | °C | |
| 1.8 MPa, Unannealed | > 76.0 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 34.0 to 67.0 | °C | |
| Injection Pressure | 68.0 to 105 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® SB9310 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Copolymer | POLYPRO® |
| Nypol® PA A3 BGE0209 NR348 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Sylvin 8205-95UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durez® 34127 | SBHPP | Phenolic | Durez® |
| LNP™ THERMOCOMP™ JF002 compound | SABIC Innovative Plastics | PESU | LNP™ THERMOCOMP™ |