Braskem PE SGD4960
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem America Inc. |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VRGRSo_BraskemPESGD4960.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SGD4960 is a high density polyethylene homopolymer especially designed for blow molding processing. It features high density and stiffness combined with high impact resistance. The minimum biobased content of this grade is 96%, determined according to ASTM D6866. Application: Bottles for food applications such as dairy products and beverages. Containers for non-food applications such as alcohol, cosmetics and lubricant oils. Process: Blow Molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.961 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.70 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 50 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance 1 | ASTM D1693 | ||
| 2.00mm, 10% Igepal, molded, F50 | 19.0 | hr | ASTM D1693 |
| 2.00mm, 100% Igepal, molded, F50 | 24.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 32.0 | MPa | ASTM D638 |
| Fracture, molding | 22.0 | MPa | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 1600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (Compression Molded) | 89 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 79.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 96 | % | ASTM D6866 |
| Note Message | |
|---|---|
| 1 . | 0.3mm notched-plaques |
| 2 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1383 P-1 | RTP Company | PPS | RTP |
| 3M™ Dyneon™ Fluoroplastic THVP 2030GZ | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroplastic |
| Bayflex® 190 RRIM (20% Mica) | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| LNP™ STAT-KON™ DEL339XF compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| ULTEM™ 4000 resin | SABIC Innovative Plastics | PEI | ULTEM™ |