TAROLOY 10
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VRCgGH_TAROLOY-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAROLOY 10 is a Polycarbonate + PBT (PC+PBT) product. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.60 to 1.0 | % | |
| Flow | 0.60 to 1.0 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.080 | % | |
| Saturation, 23°C | 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2150 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 65.0 | MPa | |
| Break | 60.0 | MPa | |
| Tensile Strain (Break) | > 100 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2300 | MPa | ISO 178 |
| Flexural Stress 2 | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 700 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 110 | °C | ISO 75-2/A |
| Continuous Use Temperature 3 | 90.0 | °C | IEC 60216 |
| Vicat Softening Temperature | 140 | °C | ISO 306/A50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow (-30 to 30°C) | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (3.00 mm) | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 110 | °C | |
| Pre-heater | 110 to 120 | °C | |
| Drying Time | |||
| -- | 2.0 | hr | |
| Pre-heater | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1.0 mm/min |
| 3 . | 20000 hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene GC20P104-08 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Flontech® FT-EK10-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| HIPOLEN P® EA 5TS | HIPOL A.D. | PP, Unspecified | HIPOLEN P® |
| Plexar® PX3940X01 | LyondellBasell Industries | PE, Unspecified | Plexar® |
| Sylvin 9077-80 White 1441 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |