Maxxam™ FR PP FR 7B01
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ FR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VRCa0N_Maxxam-FR-PP-FR-7B01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Maxxam™FR flame retardant polyolefin polymers and masterbatches meet the strict flammability requirements set by the industry, including UL 94V-2,V-0 and 5VA performance grades of UL Laboratory. In addition, the various polymers in the Maxxam FR combination are also suitable for high relative temperature index (RTI) levels. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.938 | g/cm³ | ASTM D792 |
| Specific Volume | 1.08 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (Injection Molded) | 1.0 - 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 120 | % | ASTM D638 |
| Flexural Modulus | 1380 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 43 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.18 mm) | 98.0 | °C | ASTM D648 |
| RTI Elec | UL 746 | ||
| 0.750 mm | 105 | °C | UL 746 |
| 1.50 mm | 110 | °C | UL 746 |
| 3.00 mm | 110 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 0.750 mm | 105 | °C | UL 746 |
| 1.50 mm | 110 | °C | UL 746 |
| 3.00 mm | 110 | °C | UL 746 |
| RTI | UL 746 | ||
| 0.750 mm | 105 | °C | UL 746 |
| 1.50 mm | 110 | °C | UL 746 |
| 3.00 mm | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 52 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 0.750 mm | PLC 0 | UL 746 | |
| 1.50 mm | PLC 0 | UL 746 | |
| 3.00 mm | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 0.750 mm | PLC 3 | UL 746 | |
| 1.50 mm | PLC 2 | UL 746 | |
| 3.00 mm | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750mm, all | V-2 | UL 94 | |
| 1.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 |
| Additional Information |
|---|
| Unless otherwise specified, all data listed is for natural and black colored materials. Pigments can affect properties. |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type 1, 51mm/min |
| 3 . | Type 1, 51mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Andur AL 62 DP/Curene® 110 | Anderson Development Company | PUR-Eth,aliphat | Andur |
| HONES® PPS HS-5066A | Guangdong Shunde Hones Polymer Material Co., Ltd. | PPS | HONES® |
| Latamid 66 B H-V0 | LATI S.p.A. | Nylon 66 | Latamid |
| INSTRUC FEPGF10 | Infinity LTL Engineered Compounds | FEP | INSTRUC |
| Sylvin 8200-88C Green 3208 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |