Kynar Flex® 2850-07
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Arkema |
| Trademark: | Kynar Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VQgIp8_Kynar-Flex-2850-07.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KYNAR FLEX® 2850-07 is a pelletized, semi-crystalline VF2 based copolymer. KYNAR FLEX® 2850-07 has been specifically designed for injection molded and extruded chemically resistant constructions. KYNAR FLEX® 2850-07 is easily processed and has excellent physical, mechanical, thermal and flame resistant characteristics. ADDITIONAL CHARACTERISTICS Excellent thermal stability Excellent abrasion resistance Excellent purity and chemical resistance Imprevious to UV degradation Self extinguishing material Extremely low smoke emission characteristics Pigmentable |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.77 to 1.80 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 70 to 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 31.0 to 41.4 | MPa | |
| Break, 23°C | 27.6 to 48.3 | MPa | |
| Tensile Elongation (Break, 23°C) | 30 to 200 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1030 to 1240 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 20.7 to 34.5 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 41.4 to 58.6 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 155 to 160 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 1(20°C) | 2.0E+14 | ohms·cm | ASTM D257 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (232°C, 100 sec^-1) | 1600 to 2000 | Pa·s | ASTM D3835 |
| Note Message | |
|---|---|
| 1 . | 65% R.H. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 5061R 65308 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| Sylvin 8200-95 Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Zytel® 70G13HS1L NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Comai 665-7 BL | Comai Ltda | LLDPE | Comai |
| Hanwha Total PP BI616 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |