NEOFLON™ EFEP RP-4020

Category:	Fluoropolymer , Fluoropolymer
Manufacturer:	DAIKIN AMERICA, INC.
Trademark:	NEOFLON™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	VQaRrG_NEOFLON-EFEP-RP-4020.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

EFEP RP-4020 and RP-4040 are fluoropolymers combining the excellent physical and chemical properties derived from ETFE together with the very low melting temperature characteristic of a conventional thermoplastic. These resins have a high transparency and adhere well to many kinds of plastics and inorganic materials (glass, metals) without adhesive or etching.

EFEP RP-4020 and RP-4040 offer the following advantages for a wide range of applications found in the chemical processing, semiconductor and film industries:

Very low processing temperature and excellent thermal stability

High transparency

Excellent chemical resistance

High purity

Excellent weathering

Improved heat sealing properties

Low mold shrinkage (injection molding)

Co-extrusion with other resins (nylons, EVOH, modified PE, and ETFE) without adhesive or etching

General Information
Features	High purity Good heat sealability Good adhesion Good chemical resistance Good weather resistance Definition, high Thermal stability, good Low shrinkage
Uses	Films Multilayer film Pipe fittings Bottle Container
Appearance	Clear/transparent
Forms	Particle
Processing Method	Co-extrusion molding Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.74	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (265°C/5.0 kg)	25 - 50	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	45.0	MPa	ASTM D638
Tensile Elongation (Break)	500	%	ASTM D638
Flexural Modulus	1300	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	160	°C	DSC

Optical	Nominal Value	Unit	Test Method
Transmittance (100 µm, 250 nm)	87.0	%	ASTM D1003

Injection	Nominal Value	Unit
Rear Temperature	180 - 200	°C
Middle Temperature	200 - 220	°C
Front Temperature	230 - 250	°C
Nozzle Temperature	230 - 250	°C
Mold Temperature	30.0 - 80.0	°C
Injection Pressure	50.0 - 100	MPa

Injection instructions
Injection speed: 3-15 mm/sCooling time: 10-40 sec

Resin Grade	Manufacturer	Category	Trademark
Catalyst CT/2-OR UV	Solvay Specialty Polymers	Polyolefin, Unspecified	Catalyst
Hylon® N2030GBHL	Ravago Manufacturing Americas, LLC	Nylon 6	Hylon®
Infino XF-4150	SAMSUNG SDI CO., LTD.	PPA	Infino
Kepital® TS-25HN	KEP Americas	Acetal (POM) Copolymer	Kepital®
Sylvin 9067F3 Red 6265	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin