Moplen HP515M
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VPSFxz_Moplen-HP515M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen HP515M is a polypropylene homopolymer developed for the production of transparent cast film. It is formulated with slip and anti-blocking agents. Films made with Moplen HP515M show very high transparency, a high gloss and a good printability after corona treatment. Main applications are the production of shopping bags and packaging of snacks, pasta, bakery products, books, blankets, hosiery and shirts. Moplen HP515M is suitable for food contact. For regulatory information please refer to Moplen HP515M Product Stewardship Bulletin ( PSB ). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1250 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 11 | % | |
| Break | 570 | % | |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.25 | ||
| vs. Itself - Static | 0.30 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus - MD 1(50 µm) | 800 | MPa | ASTM D882 |
| Tensile Strength - MD 2 | ASTM D882 | ||
| Yield, 50 µm | 21.0 | MPa | |
| Break, 50 µm | 32.0 | MPa | |
| Tensile Elongation - MD 3 | ASTM D882 | ||
| Yield, 50 µm | 5.0 | % | |
| Break, 50 µm | 610 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 85.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 153 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 100 µm) | 88 | ASTM D2457 | |
| Haze (100 µm) | 1.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 25 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nymax™ GMF 604 40 UV BLACK 28 | PolyOne Corporation | Nylon 6 | Nymax™ |
| Geon™ Vinyl Rigid Molding MP412 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| LNP™ THERMOCOMP™ RZ006 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Sylvin 8773-60D Brown 7383 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |
| LEXAN™ HFD1830 resin | SABIC Innovative Plastics | PC | LEXAN™ |