Terlux® HD 2802
| Category: | MABS , Methyl Methacrylate / ABS |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Terlux® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VO6efE_Terlux-HD-2802.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Terlux® HD 2802 is a standard injection molding grade based on a MABS polymer. Terlux® HD 2802 offers an unique combination of properties, such as a balanced stiffness/toughness ratio and the high transparency well known in SAN molding compositions.molding compositions. Terlux® HD 2802 is supplied only for established applications. For new HD projects we offer Terlux® HD 2822. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Apparent Density 1 | 0.59 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 220°C/10.0 kg | 2.00 | cm³/10min | |
| 220°C/21.6 kg | 17.0 | cm³/10min | |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.70 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 70.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 48.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 4.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 12 | % | ISO 527-2 |
| Tensile Creep Modulus (1000 hr) | 1250 | MPa | ISO 899-1 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 2.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 80 | kJ/m² | |
| 23°C | 120 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 94.0 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ISO 306/A50 |
| -- | 93.0 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 to 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.17 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Constant (100 Hz) | 2.90 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.016 | ||
| 1 MHz | 0.014 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Refractive Index | 1.540 | ISO 489 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Velocity | 200 | mm/sec |
| Note Message | |
|---|---|
| 1 . | With external lubricant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2100 TFE 10 | RTP Company | PEI | RTP |
| Hax™ HF 4021/TC | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| Hostalen GM 5010 T3 black | LyondellBasell Industries | HDPE | Hostalen |
| LNP™ FARADEX™ NX07344 compound | SABIC Innovative Plastics Asia Pacific | PC+ABS | LNP™ FARADEX™ |
| Lupolen 3621 M RM Black Powder | LyondellBasell Industries | MDPE | Lupolen |