Terblend® N 3158
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Terblend® N |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VNsPFx_Terblend-N-3158.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Terblend® N 3158 is an 9% mineral-filled ABS/PA blend with good dimensional stability, enhanced rigidity and excellent heat resistance, so that this grade can be applied for online-painting. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/10.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 1.1 to 1.4 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 50.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 23°C | 3.0 | % | |
| Break, 23°C | > 10 | % | |
| Flexural Modulus | 3000 | MPa | ISO 178 |
| Flexural Stress | 88.0 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation - MD (Break) | > 10 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 160 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 132 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 92.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 245 | °C | ASTM D1525 1 |
| -- | 160 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 7.5E-3 | ||
| 1 MHz | 0.015 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Velocity | 40 | mm/sec |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tekucom SC GF 20 C | TEKUMA Kunststoff GmbH | PP, Unspecified | Tekucom |
| Niuk 20GP17 | Shanghai Niuk New Plastic Technology Co., Ltd. | ABS | Niuk |
| EvoSource™ ABS 4535 (China) | MBA Polymers | ABS | EvoSource™ |
| Karina IVORY PVC COMPOUND -E711D35/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LightSpan® LS-6946 | NuSil Technology | Silicone | LightSpan® |