Lanufene LLF 181H
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Ras Lanuf Oil & Gas Processing Company (RASCO) |
| Trademark: | Lanufene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VMwgQ1_Lanufene-LLF-181H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LANUFENE LLF 181H is a linear low density polyethylene for general purpose blown film extrusion with high mechanical properties and good process-ability. LANUFENE LLF 181H contains slip additive and anti-blocking agent. The film produced from this resin characteristically exhibits good toughness, high tensile properties, outstanding puncture resistance and good optical properties. LANUFENE LLF 181H is recommended for the manufacture of general purpose blown films such as industrial liners, food packaging and agricultural film. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Ultimate) | 21.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 700 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 38 µm | 220 | MPa | |
| 1% Secant, TD : 38 µm | 260 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 38 µm | 40.0 | MPa | |
| TD : Break, 38 µm | 32.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm | 700 | % | |
| TD : Break, 38 µm | 750 | % | |
| Dart Drop Impact (38 µm) | 150 | g | ASTM D1709A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 99.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm) | 55 | ASTM D2457 | |
| Haze (38.0 µm) | 12 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GF13-66 22LH-NBK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Nypol® PA A3 TZ NTLA010 NR338 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Durethan® BKV 15 G H2.0 900051 | LANXESS GmbH | Nylon 6 | Durethan® |
| Karina BROWN PVC COMPOUND -E 933-36/556-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Integra™ 9060 FR | PolySource, LLC | PK | Integra™ |