LNP™ LUBRICOMP™ RFL32 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VLtCsI_LNP-LUBRICOMP-RFL32-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RFL32 is a compound based on Nylon 66 containing 10% Glass Fiber, 15% PTFE. Added feature of this material includes: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RFL-4032 Product reorder name: RFL32 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.50 to 0.70 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.64 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.97 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5640 | MPa | ASTM D638 |
| -- | 5500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 107 | MPa | ASTM D638 |
| Break | 103 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.8 | % | ASTM D638 |
| Break | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 5300 | MPa | ASTM D790 |
| -- 5 | 5020 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 159 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 46 | J/m | ASTM D256 |
| 23°C 7 | 4.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 390 | J/m | ASTM D4812 |
| 23°C 8 | 25 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.58 | J | ASTM D3763 |
| -- | 1.56 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 260 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 257 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 246 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 240 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.7E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VICTREX® PEEK 600P | Victrex plc | PEEK | VICTREX® PEEK |
| NuSil CV9-1142 | NuSil Technology | Silicone | NuSil |
| Lutene® XL2700BK | LG Chem Ltd. | PE, Unspecified | Lutene® |
| POLIMAXX 2440TC | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |
| TOTAL Polypropylene PPH 3485WZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |