TECACOMP® PA66 TC grey 4057
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VLpIsl_TECACOMPPA66TCgrey4057.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.91 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 24 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.2 | % | ISO 294-4 |
| Flow | 1.1 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.90 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9900 | MPa | ISO 527-2/50 |
| Tensile Stress | 80.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 1.4 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 15 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 189 | °C | ISO 75-2/A |
| Glass Transition Temperature | 50.0 | °C | DIN 53765 |
| Melting Temperature | 255 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1090 | J/kg/°C | DIN EN 821 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 1 | 1.1 | W/m/K | DIN EN 821 |
| -- 2 | 1.3 | W/m/K | DIN EN 821 |
| Service Temperature | |||
| long term | 110 | °C | |
| short term | 170 | °C | |
| Thermal Diffusivity | DIN EN 821 | ||
| In-plane | 0.500 | cSt | DIN EN 821 |
| Through-plane | 0.620 | cSt | DIN EN 821 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | DIN EN 61340 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | DIN EN 61340 |
| Dielectric Strength | 27 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (0.8 mm) | V-0 | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 260 - 310 | °C | |
| Mold Temperature | 90 - 150 | °C |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santron IMS2000 GLITTER | Bhansali Engineering Polymers Limited | SAN | Santron |
| SAMAT 5003N1 | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| Sylvin 8983-80 White 1196 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Xuchuan XCS-3086 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Next Nylon 66 Prime Series PST-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |