Ultramid® A3WG7 CR BK564
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VLMUCV_Ultramid-A3WG7-CR-BK564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fibre reinforced and heat aging resistance injection moulding grade for industrial items such as gear wheels, solenoid valve housings, cable attachments, automotive fuel distributors and components for automotive gearshift. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.41 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 22.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.1 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption (Saturation, 23°C) | 5.0 to 5.5 | -- | % | ISO 62 |
| Mold Shrinkage - constrained 1 | 0.40 to 0.45 | -- | % |
| Additional Information | Dry | Conditioned | ||
|---|---|---|---|---|
| Polymer Abbreviation | PA66-GF35 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11400 | 7600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 200 | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.1 | 4.4 | % | ISO 527-2 |
| Flexural Modulus | 10800 | 7200 | MPa | ISO 178 |
| Flexural Stress | 300 | 200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 8.0 | 8.0 | kJ/m² | |
| 23°C | 10 | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 65 | 63 | kJ/m² | |
| 23°C | 85 | 88 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test box with central gating, dimensions of base (107*47*1,5) mm, processing conditions: TM = 290°C, TW = 80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 6 Prime Series NMS1-01 S.GY. | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Network Polymers SMMA MS 221 | Network Polymers, Inc. | Acrylic (SMMA) | Network Polymers SMMA |
| HydroMed™ D6 | AdvanSource Biomaterials Corp. | PUR-Ether | HydroMed™ |
| Infino GP-8200G | SAMSUNG SDI CO., LTD. | PPE | Infino |
| LNP™ THERMOCOMP™ DX11354X compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |