| PC/PBT-Blend |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 250°C/5.0 kg | 37 | g/10 min | |
| 260°C/2.16 kg | 22 | g/10 min | |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.70 to 1.0 | % | |
| Flow | 0.70 to 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 55.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 2200 | MPa | ISO 178 |
| Flexural Stress | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 15 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 107 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ISO 306/A50 |
| -- | 123 | °C | ISO 306/B50 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS ZF5551 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Nylene® 134 HS | Custom Resins Group | Nylon 66 | Nylene® |
| Comco PEEK mod. | Comco-Plastic GmbH | PEEK | Comco |
| Emulprene® 1011CR | INSA | SBR, Emulsion | Emulprene® |
| Axiall PVC 7465A | Axiall Corporation | PVC, Rigid | Axiall PVC |