Toraycon® 5107G
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toraycon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VKrTRx_Toraycon-5107G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toraycon® 5107G is a Polybutylene Terephthalate (PBT) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.49 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 1.0 | % | |
| Flow : 3.00 mm 2 | 0.40 | % | |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8400 | MPa | ISO 527-2 |
| Tensile Stress (23°C) | 125 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 7900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 195 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 208 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 100°C) | 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length 3(250°C, 1.00 mm) | 7.00 | cm | Internal Method |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | 93 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badamid® LC70 M40 | Bada AG | Nylon 6+Nylon 66/6 | Badamid® |
| FHR Polypropylene 13T10Acs279 | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| Elastron® G G300.A85.B | Elastron USA, Inc. | SEBS | Elastron® G |
| PLUSTEK PD120BK11 | Polyram Ram-On Industries | Nylon 12 | PLUSTEK |
| PolyBlend™ 1100 75A | CardioTech International, Inc. | PUR, Unspecified | PolyBlend™ |