Hostacom 65F4-3 conventional melt flow, 2,200 MPa flexural modulus, 30% talc-filled polypropylene homopolymer is designed for high heat stability, high rigidity, excellent chemical resistance and improved surface quality of molded parts. |
General Information | |
---|---|
Filler / Reinforcement |
|
Features |
|
Uses |
|
Forms |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
Molding Shrinkage - Flow (23°C, 48 hr, 3.20 mm) | 1.1 | % | ASTM D955 |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength | ASTM D638 | ||
Yield | 30.0 | MPa | |
Break | 19.0 | MPa | |
Tensile Elongation | ASTM D638 | ||
Yield | 6.0 | % | |
Break | 35 | % | |
Flexural Modulus - Tangent 1 | 2200 | MPa | ASTM D790A |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (23°C) | 27 | J/m | ASTM D256A |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (0.45 MPa, Unannealed) | 111 | °C | ASTM D648 |
Note Message | |
---|---|
1 . | 1.3 mm/min |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
VITAMIDE® BR36GY6151 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
Utomer UT860D | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyester | Utomer |
AKROMID® B3 2 RM-D black (3254) | AKRO-PLASTIC GmbH | Nylon 6+ABS | AKROMID® |
AMTOPP PL30 | Inteplast Group | PP, Unspecified | AMTOPP |
Kingfa MAC-501 | Kingfa | PC+ABS | Kingfa |