WPP PP PPC3225
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VK5P3O_WPP-PP-PPC3225.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WPP PP PPC3225 is a polypropylene copolymer (PP Copoly) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 22.0 | MPa | ASTM D638 |
| Flexural Modulus - Tangent 2 | 1000 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 87.8 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 204 - 210 | °C | |
| Middle Temperature | 210 - 216 | °C | |
| Front Temperature | 216 - 221 | °C | |
| Nozzle Temperature | 221 - 227 | °C | |
| Mold Temperature | 15.6 - 48.9 | °C | |
| Injection Pressure | 4.14 - 7.58 | MPa | |
| Holding Pressure | 1.03 - 4.14 | MPa | |
| Back Pressure | 0.517 - 1.03 | MPa | |
| Clamp Tonnage | 3.4 - 5.5 | kN/cm² | |
| Cushion | 3.18 - 6.35 | mm |
| Injection instructions |
|---|
| Injection Speed: 1.5 to 2.5 in/sZone 4 Temperature: 420 to 430°FHot Runner Temperature: 410 to 440°FHydraulic Oil Temperature: 110 to 125°FShot Capacity vs. Barrel Capacity: 2.5 to 4Screw Decompression: 0.1 to 0.25 in |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ 7055 BK100 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| Versalloy™ XL 9055X-9 | PolyOne Corporation | TPE | Versalloy™ |
| Dynacom CT-130 V2 | Dynachem Co. Ltd. | PP Copolymer | Dynacom |
| Polyrocks EP8400X105V-3 | Polyrocks Chemical Co., Ltd | XLPE | Polyrocks |
| Sylvin 8950-90 Grey 9530 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |