Generic ABS - Stainless Steel Fiber
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VIVo9p_Generic-ABS---Stainless-Steel-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ABS - Stainless Steel Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.09 - 1.52 | g/cm³ | ASTM D792 |
| 23°C | 1.11 - 1.16 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.48 - 0.64 | % | ASTM D955 |
| 23°C | 0.18 - 0.56 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.20 - 0.31 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2210 - 3170 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield, 23°C | 37.6 - 50.5 | MPa | ASTM D638 |
| Yield, 23°C | 37.7 - 40.2 | MPa | ISO 527-2 |
| Fracture, 23°C | 39.1 - 50.6 | MPa | ASTM D638 |
| 23°C | 27.6 - 37.9 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 1.8 - 6.1 | % | ASTM D638 |
| Fracture, 23°C | 2.0 - 8.6 | % | ASTM D638 |
| Flexural Modulus | |||
| 23°C | 2400 - 3160 | MPa | ASTM D790 |
| 23°C | 2500 - 2820 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 43.8 - 89.7 | MPa | ASTM D790 |
| 23°C | 59.8 - 66.4 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 27 - 60 | J/m | ASTM D256 |
| 23°C | 7.0 - 7.5 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 150 - 320 | J/m | ASTM D256 |
| 23°C | 18 - 20 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 96.3 - 107 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 86.7 - 141 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 78.0 - 80.2 | °C | ISO 75-2/A |
| CLTE - Flow | 8.1E-5 - 8.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.5 - 2.5E+8 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 0.10 - 2.5E+8 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.1 - 82.2 | °C | |
| Drying Time | 2.0 - 9.0 | hr | |
| Suggested Max Moisture | 0.075 - 0.10 | % | |
| Rear Temperature | 215 - 260 | °C | |
| Middle Temperature | 228 - 260 | °C | |
| Front Temperature | 215 - 261 | °C | |
| Nozzle Temperature | 210 | °C | |
| Processing (Melt) Temp | 225 - 246 | °C | |
| Mold Temperature | 65.6 - 82.2 | °C | |
| Injection Pressure | 85.9 - 103 | MPa | |
| Back Pressure | 0.258 - 0.517 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ABS - Stainless Steel FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® CP-13235 | Teknor Apex Company | TPE | Monprene® |
| Amilan® CM3211G35UB1 | Toray Resin Company | Nylon 66 | Amilan® |
| CYCOLAC™ MG38N resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| Ferro PP TPP40AJ35BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Plaslube® TPX-PA6/6-98020 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |