Order Products : sales@su-jiao.com
Infino NH-1015U
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VI9nxk_InfinoNH1015U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Infino NH-1015U is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Infino NH-1015U applications include electrical/electronic applications and electrical appliances. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 34 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.34 - 0.42 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.36 - 0.44 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.36 - 0.44 | % | ISO 2577 |
| Traffic : 3.20mm | 0.34 - 0.42 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 118 | ASTM D785 | |
| R scale | 118 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2400 | MPa | ASTM D638 |
| -- | 2400 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 59.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 55.0 | MPa | ASTM D638 |
| Fracture | 56.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 50 | % | ASTM D638 |
| Fracture | 50 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2500 | MPa | ASTM D790 |
| -- 6 | 2500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 88.0 | MPa | ASTM D790 |
| -- 8 | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 45 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 540 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 180 | J/m | ASTM D256 |
| 23°C 10 | 40 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.40mm | 86.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 82.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 98.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ LDPE PG 7004 (Injection Molding) | The Dow Chemical Company | LDPE | DOW™ LDPE |
| UNITREX® Rg-30 | Nytef Plastics, Ltd. | PEEK | UNITREX® |
| Karina IVORY PVC COMPOUND 650-35/1-A-EX | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petrothene® GA501150X01 | LyondellBasell Industries | LLDPE | Petrothene® |
| EPAMOULD 665A56 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |