Bakelite® PF 6510
| Category: | Phenolic , Phenolic |
| Manufacturer: | Hexion Inc. |
| Trademark: | Bakelite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VHW3yr_Bakelite-PF-6510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description Phenolic moulding compound, inorganically filled, glass fibre reinforced, high dimensional stability at raised temperature, good media resistance, heat-resistant Application Areas Thermally and mechanically highly stressed parts in automotive field, insulating flanges, water pump housings |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.70 | g/cm³ | ISO 1183 |
| Apparent Density | 0.74 | g/cm³ | ISO 60 |
| Molding Shrinkage 1 | 0.20 | % | ISO 2577 |
| Water Absorption - 24h/23C | 12.0 | mg | ISO 62 |
| Post Shrinkage 2 | 0.050 | % | ISO 2577 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 15.0 | MPa | |
| Compression Molding Temperature | 160 to 190 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 16000 | MPa | ISO 527-2/1 |
| Tensile Stress | 100 | MPa | ISO 527-2/5 |
| Flexural Modulus | 16000 | MPa | ISO 178 |
| Flexural Stress 3 | 210 | MPa | ISO 178 |
| Compressive Stress | 250 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 16 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (8.0 MPa, Unannealed) | 175 | °C | ISO 75-2/C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength 4(1.00 mm) | 33 | kV/mm | IEC 60243-1 |
| Relative Permittivity (100 Hz) | 6.00 | IEC 60250 | |
| Dissipation Factor (100 Hz) | 0.050 | IEC 60250 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 to 75.0 | °C | |
| Nozzle Temperature | 80.0 to 100 | °C | |
| Processing (Melt) Temp | 80.0 to 100 | °C | |
| Mold Temperature | 160 to 190 | °C | |
| Injection Pressure | > 15.0 | MPa | |
| Back Pressure | 0.500 to 2.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Injection |
| 2 . | Injection |
| 3 . | 2.0 mm/min |
| 4 . | short term, electrode layout P25mm/P25mm in transformer oil equivalent to IEC 60296 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PEEK KD2000 Injection Molded Shape | Polymics, Ltd. | PEEK | Pyramid™ PEEK |
| Shuman PP 502C | Shuman Plastics, Inc. | PP Copolymer | Shuman PP |
| VESTAMID® L X7293 | Evonik Industries AG | Nylon 12 | VESTAMID® L |
| BIOH™ Polyol X-0005 | Cargill Industrial Bio-Products | Biodeg Polymers | BIOH™ Polyol |
| Ferro PP TPP10AN52NA | Ferro Corporation | PP, Unspecified | Ferro PP |