TAROLOX 10 X0
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VGqgGP_TAROLOX-10-X0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PBT self extinguishing UL94 V0, good flow, good mechanical and thermal properties. UL94 V0 approuved all colors at 0,97 mm. UL746B approved. Available: all colors, heat stabilized (H), release agent (W), without PBDE/PBDF. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 to 1.43 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.5 to 2.0 | % | |
| Across Flow | 1.5 to 2.0 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.060 | % | ASTM D570, ISO 62 |
| Saturation | 0.35 | % | ASTM D570 |
| Saturation, 23°C | 0.35 | % | ISO 62 |
| Granule Humidity | < 0.050 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 60.0 | MPa | |
| Break | 55.0 | MPa | |
| Tensile Elongation (Break) | > 50 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2700 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- 1 | 100 | MPa | ISO 178 |
| -- 2 | 80.0 | MPa | ISO 178 |
| Yield | 100 | MPa | ASTM D790 |
| Break | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3(23°C) | 3.5 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 4 | ISO 179, ASTM D256 | ||
| -20°C | 40 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Notched Izod Impact | |||
| -20°C, 3.20 mm | 40 | J/m | ISO 180, ASTM D256 |
| 23°C, 3.20 mm | 50 | J/m | ASTM D256, ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 75.0 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | |||
| -- | 75.0 | °C | UL 746B |
| -- 5 | 90.0 | °C | IEC 60216 |
| -- 6 | 120 | °C | IEC 60216 |
| -- 7 | 130 | °C | IEC 60216 |
| -- 8 | 160 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 205 | °C | ASTM D1525, ISO 306/A50 10 9 |
| -- | 190 | °C | ASTM D1525, ISO 306/B50 11 10 |
| Ball Pressure Test (165°C) | Pass | VDE 0470 | |
| Melting Temperature | 220 to 225 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 22 | kV/mm | ASTM D149 |
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 275 | V | |
| Solution B | 175 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 0.970 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 28 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Pre-heater | 120 to 130 | °C | |
| Drying Time | |||
| -- | 1.0 to 2.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Yield |
| 2 . | Break |
| 3 . | 6x4x50 mm |
| 4 . | 6x4x50 mm |
| 5 . | 20000 hrs |
| 6 . | Heat Stabilized, 20000 hrs |
| 7 . | Short Term |
| 8 . | Heat Stabilized, Short Term |
| 9 . | Rate A (50°C/h), Loading 1 (10 N) |
| 10 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badamid® LA70 GF30 H | Bada AG | Nylon 66 | Badamid® |
| Braskem PP C144-04NA | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| Geon™ HTX M6309 | PolyOne Corporation | PVC Alloy | Geon™ HTX |
| SCHULADUR® PCR GF30 | A. Schulman Inc. | Polyester, TP | SCHULADUR® |
| Sylvin 9604-85 Clear Red 6254 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |