Durethan® AKV 35 HR H2.0 901510
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS Corporation |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VGpZkP_Durethan-AKV-35-HR-H2-0-901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 35 % glass fibers, injection molding, heat-aging stabilized, hydrolysis stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | ||||
| -- | 1.41 | -- | g/cm³ | ASTM D792 |
| 23°C | 1.41 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 300°C, 2.00 mm 1 | 1.1 | -- | % | |
| Across Flow : 120°C, 2 hr, 2.00 mm 2 | 0.090 | -- | % | |
| Flow : 300°C, 2.00 mm 3 | 0.38 | -- | % | |
| Flow : 120°C, 2 hr, 2.00 mm 4 | 0.060 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.2 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C 5 | 11000 | 6090 | MPa | ASTM D638 |
| 23°C | 11500 | 7800 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Break, 23°C | 190 | -- | MPa | ASTM D638 |
| Break, 23°C | 195 | 135 | MPa | ISO 527-2/5 |
| Tensile Elongation | ||||
| Break, 23°C | 3.0 | -- | % | ASTM D638 |
| Break, 23°C | 3.1 | 6.0 | % | ISO 527-2/5 |
| Flexural Modulus | ||||
| 23°C | 10000 | -- | MPa | ASTM D790 |
| 23°C 6 | 10700 | 7000 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 23°C | 290 | -- | MPa | ASTM D790 |
| 3.5% Strain 7 | -- | 180 | MPa | ISO 178/A |
| 23°C 8 | 305 | 210 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 9(23°C) | 3.8 | 6.0 | % |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 10(> 1.00 mm) | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66, GHRW, 14-110, GF30 | -- | ISO 1874 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | < 10 | < 10 | kJ/m² | |
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | 13 | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 75 | 80 | kJ/m² | |
| 23°C | 85 | 85 | kJ/m² | |
| Notched Izod Impact | ||||
| 23°C, 3.18 mm | 140 | -- | J/m | ASTM D256 |
| -30°C | 10 | 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 65 | -- | kJ/m² | |
| 23°C | 75 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed, 3.99 mm | > 249 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.99 mm | > 249 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 245 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | ||||
| -- | > 230 | -- | °C | ISO 306/B50 |
| -- | 255 | -- | °C | ISO 306/B120 |
| Melting Temperature 11 | 262 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | |||
| 23°C, 1.00 mm | 35 | -- | kV/mm | |
| 23°C, 3.00 mm | 40 | 35 | kV/mm | |
| Dielectric Constant | IEC 60250 | |||
| 23°C, 50 Hz 12 | 4.00 | 10.0 | ||
| 23°C, 1 MHz 13 | 4.00 | 4.00 | ||
| 23°C, 100 Hz | 3.90 | -- | ||
| 23°C, 1 MHz | 3.60 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 23°C, 50 Hz | 6.0E-3 | 1.0 | ||
| 23°C, 100 Hz | 0.010 | -- | ||
| 23°C, 1 MHz | 0.015 4.0E-3 | 0.18 | ||
| Comparative Tracking Index (Solution A) | 425 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 14 | 26 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 1.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Pull Rate: 2 mm/min; 50% RH |
| 10 . | US-FMVSS302 |
| 11 . | 10°C/min |
| 12 . | Tinfoil Electrodes |
| 13 . | Tinfoil Electrodes |
| 14 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 400 HI FR | RTP Company | PS (HIPS) | RTP |
| elitel UE3660 | UNITIKA Plastics Division | TPC-ET | elitel |
| Karina PVC COMPOUND - IVORY E-105900-35/ 1-B-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petro Rabigh PE FS350A | Rabigh Refining & Petrochemical Co. | LLDPE | Petro Rabigh PE |
| ALFATER XL® A90E 2GP0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |